- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.66
- 吸水率 [%]: 0.33
- 弯曲模量 [MPa]: 9.50
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.030 % | 0.030 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.33 % @Temperature 23.0 °C | 0.33 % @Temperature 73.4 °F | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on tensile bar; SABIC Method | ||
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | on tensile bar; SABIC Method | ||
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 265 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, H358/30 | 140 MPa | 20300 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 | ||
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 195 MPa | 28300 psi | break, 2 mm/min; ISO 178 | ||
| Flexural Modulus | 9.50 GPa | 1380 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | ||
| 40.0 kJ/m² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
| 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |||
| Taber Abrasion, mg/1000 Cycles | 45 @Load 1.00 kg | 45 @Load 2.20 lb | CS-17; SABIC Method | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.4 @Frequency 50.0 - 60.0 Hz | 3.4 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |||
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | ||
| Dissipation Factor | 0.0015 @Frequency 50.0 - 60.0 Hz | 0.0015 @Frequency 50.0 - 60.0 Hz | IEC 60250 | ||
| 0.0131 @Frequency 1.00e+6 Hz | 0.0131 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 11.1 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 50.0 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | ||
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft²-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | ||
| Vicat Softening Point | 200 °C | 392 °F | Rate B/50; ISO 306 | ||
| 200 °C | 392 °F | Rate B/120; ISO 306 | |||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL 94 by SABIC-IP | ||
| Oxygen Index | 31 % | 31 % | LOI; ISO 4589 | ||
| Glow Wire Test | 960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | Glow Wire Flammability Index; IEC 60695-2-12 | ||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||