- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.2
- 缺口冲击强度: 7.13
- 拉伸强度 [MPa]: 60.0
- 断裂伸长率 [%]: 92.0
- 弯曲模量 [MPa]: 2.25
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 265 °C | 12 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D 1238 |
| 12 g/10 min @Load 2.16 kg, Temperature 265 °C | 12 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 133 % | 133 % | 50 mm/min; ISO 527 |
| 135 % | 135 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 5.8 % | 5.8 % | 50 mm/min; ISO 527 |
| 6.3 % | 6.3 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 7.13 J/cm @Temperature 23.0 °C | 13.4 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 104 µm/m-°C @Temperature -40.0 - 40.0 °C | 57.8 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 100 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm | 223 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 126 °C | 259 °F | Rate B/50; ASTM D 1525 |
| 126 °C | 259 °F | Rate B/50; ISO 306 | |
| 126 °C | 259 °F | Rate B/120; ISO 306 | |
| Optical Properties | Metric | English | Comments |
| Haze | <= 2.0 % @Thickness 2.54 mm | <= 2.0 % @Thickness 0.100 in | ASTM D 1003 |
| Transmission, Visible | 89 % @Thickness 2.54 mm | 89 % @Thickness 0.100 in | ASTM D 1003 |