- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.4
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs at 23°C |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | |
| Elongation at Break | 1.8 % | 1.8 % | |
| Modulus of Elasticity | 4.40 GPa | 638 ksi | |
| Flexural Strength | 100 MPa | 14500 psi | |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C | 25.0 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | 0.455 MPa |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 110 °C | 230 °F | |