- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.6
- 弯曲强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 8.00
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM-D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM-D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM-D785 |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM-D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM-D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM-D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM-D256 |
| Taber Abrasion, mg/1000 Cycles | 28 | 28 | CS-17; ASTM-D1044 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM-D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm | 635 kV/in @Thickness 0.0787 in | ASTM-D149 |
| Arc Resistance | 130 sec | 130 sec | Tungsten electrode; ASTM-D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM-D696 |
| Melting Point | 255 °C | 491 °F | DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Thermal Index; UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM-D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |