- 缺口冲击强度: 0.609
- 拉伸强度 [MPa]: 134.0
- 弯曲模量 [MPa]: 17.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 134 MPa | 19400 psi | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 214 MPa | 31000 psi | at Break, (50.8 mm Span) 1mm/min; ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2490 ksi | (50.8 mm Span) 1mm/min; ASTM D790 |
| Izod Impact, Notched | 0.609 J/cm | 1.14 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.5 ohm-cm | 1.5 ohm-cm | ASTM D257 |
| Surface Resistance | 3000 ohm | 3000 ohm | ASTM D257 |
| Static Decay | <= 0.010 sec | <= 0.010 sec | 5000V to <50V; FTMS101B |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C @Thickness 6.35 mm | 399 °F @Thickness 0.250 in | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 238 - 254 °C | 460 - 489 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 469 - 500 °F | |
| Front Barrel Temperature | 249 - 266 °C | 480 - 511 °F | |
| Nozzle Temperature | 243 - 260 °C | 469 - 500 °F | |
| Melt Temperature | 249 - 266 °C | 480 - 511 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Moisture Content | 0.020 % | 0.020 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi | |
| Clamp Pressure | 41.0 - 83.0 MPa | 5950 - 12000 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | Suggested |
| Vent Depth | 0.00250 - 0.00380 cm | 0.000984 - 0.00150 in | |
| Screw Speed | 50 - 80 rpm | 50 - 80 rpm | |