- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 4.0
- 弯曲强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 3.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183-87 |
| Filler Content | 19 % | 19 % | |
| Linear Mold Shrinkage | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | ISO 527-93 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527-93 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178-93 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-93 |