- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 0.32
- 断裂伸长率 [%]: 97.0
- 弯曲强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 4.00
- 热变形温度 [℃]: 259.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 - 1.58 g/cc | 0.0412 - 0.0571 lb/in³ | Average value: 1.42 g/cc Grade Count:7 |
| Filler Content | 20.0 % | 20.0 % | Average value: 20.0 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00300 - 0.00600 cm/cm | 0.00300 - 0.00600 in/in | Average value: 0.00433 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 62.0 - 100 MPa | 8990 - 14500 psi | Average value: 93.8 MPa Grade Count:7 |
| Elongation at Break | 1.80 - 3.30 % | 1.80 - 3.30 % | Average value: 2.34 % Grade Count:7 |
| Modulus of Elasticity | 5.50 - 8.00 GPa | 798 - 1160 ksi | Average value: 7.05 GPa Grade Count:6 |
| Flexural Yield Strength | 97.0 - 155 MPa | 14100 - 22500 psi | Average value: 142 MPa Grade Count:7 |
| Flexural Modulus | 4.00 - 7.40 GPa | 580 - 1070 ksi | Average value: 5.96 GPa Grade Count:7 |
| Izod Impact, Notched | 0.320 - 1.10 J/cm | 0.600 - 2.06 ft-lb/in | Average value: 0.618 J/cm Grade Count:4 |
| 0.32034 - 1.00 J/cm @Temperature -40.0 - -40.0 °C | 0.60013 - 1.87 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.660 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 2.56 - 430 J/cm | 4.80 - 806 ft-lb/in | Average value: 112 J/cm Grade Count:4 |
| 2.1356 - 2.1356 J/cm @Temperature -40.0 - -40.0 °C | 4.0009 - 4.0009 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 2.14 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 5.00 - 8.00 kJ/m² | 2.38 - 3.81 ft-lb/in² | Average value: 5.83 kJ/m² Grade Count:6 |
| Charpy Impact Unnotched | 3.00 - 5.00 J/cm² | 14.3 - 23.8 ft-lb/in² | Average value: 3.50 J/cm² Grade Count:6 |
| 3.00 - 3.00 J/cm² @Temperature -30.0 - -30.0 °C | 14.3 - 14.3 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.00 J/cm² Grade Count:1 | |
| Charpy Impact, Notched | 0.500 - 0.850 J/cm² | 2.38 - 4.05 ft-lb/in² | Average value: 0.608 J/cm² Grade Count:6 |
| 0.700 - 0.700 J/cm² @Temperature -30.0 - -30.0 °C | 3.33 - 3.33 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.700 J/cm² Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | Average value: 1.00e+15 ohm-cm Grade Count:3 |
| Surface Resistance | 1.00e+15 - 1.00e+17 ohm | 1.00e+15 - 1.00e+17 ohm | Average value: 3.70e+16 ohm Grade Count:3 |
| Dielectric Strength | 19.7 - 41.0 kV/mm | 500 - 1040 kV/in | Average value: 27.1 kV/mm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 283 - 285 °C | 541 - 545 °F | Average value: 284 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 - 272 °C | 498 - 522 °F | Average value: 265 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 - 256 °C | 381 - 493 °F | Average value: 232 °C Grade Count:7 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | Average value: 302 °C Grade Count:7 |
| Mold Temperature | 80.0 - 175 °C | 176 - 347 °F | Average value: 114 °C Grade Count:7 |
| Drying Temperature | 95.0 - 150 °C | 203 - 302 °F | Average value: 106 °C Grade Count:7 |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Average value: 5.00 hour Grade Count:7 |
| Moisture Content | 0.0300 % | 0.0300 % | Average value: 0.0300 % Grade Count:6 |