- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 1.0
- 弯曲模量 [MPa]: 4.76
- 硬度: 118.0
- 热变形温度 [℃]: 264.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D 792 | ||
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | ||
| Filler Content | 20 % | 20 % | Glass fiber reinforcement | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM D 785 | ||
| Tensile Strength at Break | 87.0 MPa @Temperature 23.0 °C | 12600 psi @Temperature 73.4 °F | ASTM D 638 | ||
| 90.0 MPa @Temperature 23.0 °C | 13100 psi @Temperature 73.4 °F | ISO 527 | |||
| Elongation at Break | 2.8 % @Temperature 23.0 °C | 2.8 % @Temperature 73.4 °F | ISO 527 | ||
| 3.3 % @Temperature 23.0 °C | 3.3 % @Temperature 73.4 °F | ASTM D 638 | |||
| Tensile Modulus | 5.50 GPa @Temperature 23.0 °C | 798 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 140 MPa @Temperature 23.0 °C | 20300 psi @Temperature 73.4 °F | ISO 178 | ||
| 142 MPa @Temperature 23.0 °C | 20600 psi @Temperature 73.4 °F | ASTM D 790 | |||
| Flexural Modulus | 4.76 GPa @Temperature 23.0 °C | 690 ksi @Temperature 73.4 °F | ASTM D 790 | ||
| 4.80 GPa @Temperature 23.0 °C | 696 ksi @Temperature 73.4 °F | ISO 178 | |||
| Izod Impact, Notched | 1.00 J/cm @Temperature -40.0 °C | 1.87 ft-lb/in @Temperature -40.0 °F | ASTM D 256 | ||
| 1.10 J/cm @Temperature 23.0 °C | 2.06 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |||
| Izod Impact, Unnotched | 9.20 J/cm @Temperature 23.0 °C | 17.2 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.850 J/cm² @Temperature 23.0 °C | 4.05 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 283 °C | 541 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 264 °C | 507 °F | ASTM D 648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | ASTM D 648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 300 °C | 572 °F | Optimum | ||
| 295 - 310 °C | 563 - 590 °F | ||||
| Mold Temperature | 160 °C | 320 °F | Optimum | ||
| 150 - 175 °C | 302 - 347 °F | ||||
| Drying Temperature | 120 - 150 °C | 248 - 302 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| DuPont Product Category | Food Contact Resins | ||||
| Glass Reinforced Resins | |||||
| Toughened Resins | |||||
| Features | Food Contact Acceptable | ||||
| Toughness, Good | |||||
| Form | Pellets | ||||
| Part Marking Code | >PCT-IGF20< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Region | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | PCT-IGF20 | ISO 1043 | |||
| Uses | Food Applications, Non-specific | ||||
| Food Service Applications | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.