- 密度 [g/cm3]: 1.22
- 拉伸强度 [MPa]: 42.0
- 热变形温度 [℃]: 73.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.22 g/cc | 0.0441 lb/in³ | |
Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min |
Elongation at Break | >= 50 % | >= 50 % | |
Elongation at Yield | 4.1 % | 4.1 % | |
Tensile Modulus | 1.30 GPa | 189 ksi | 1mm/min |
Charpy Impact Unnotched | NB | NB | |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
Charpy Impact, Notched | 6.10 J/cm² | 29.0 ft-lb/in² | Partial Break |
0.590 J/cm² @Temperature -30.0 °C | 2.81 ft-lb/in² @Temperature -22.0 °F | ||
Thermal Properties | Metric | English | Comments |
CTE, linear | 97.0 µm/m-°C @Temperature 20.0 °C | 53.9 µin/in-°F @Temperature 68.0 °F | in flow direction |
CTE, linear, Transverse to Flow | 73.0 µm/m-°C @Temperature 20.0 °C | 40.6 µin/in-°F @Temperature 68.0 °F | |
Melting Point | 224 °C | 435 °F | |
Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | |
Vicat Softening Point | 77.0 °C | 171 °F | |
Glass Transition Temp, Tg | 84.0 °C | 183 °F | |
Processing Properties | Metric | English | Comments |
Melt Temperature | 275 - 295 °C | 527 - 563 °F |