- 密度 [g/cm3]: 1.2
- 拉伸强度 [MPa]: 56.0
- 热变形温度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 5.5 % | 5.5 % | |
| Tensile Modulus | 1.97 GPa | 286 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | |
| 0.770 J/cm² @Temperature -30.0 °C | 3.66 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Strength | 17.3 kV/mm | 439 kV/in | |
| Dissipation Factor | 0.0080 @Frequency 1e+6 Hz | 0.0080 @Frequency 1e+6 Hz | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 68.0 µm/m-°C @Temperature 20.0 °C | 37.8 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 1.38 J/g-°C | 0.330 BTU/lb-°F | |
| Melting Point | 249 °C | 480 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | |
| Vicat Softening Point | 110 °C | 230 °F | |
| Glass Transition Temp, Tg | 113 °C | 235 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |