- 拉伸强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.317
- 脆化温度 [℃]: -68.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.924 g/cc | 0.924 g/cc | ASTM D792 |
| ESCR 100% Igepal® | 250 hour | 250 hour | Condition C; ASTM D1693 |
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | 2"/min; ASTM D638 |
| Elongation at Break | 175 % | 175 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.317 GPa | 46.0 ksi | at 1% secant modulus; ASTM D790 |
| Falling Dart Impact | 28.5 J | 21.0 ft-lb | -40°C; ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -68.0 °C | -90.4 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 122 °C | 252 °F | |