- 熔体流动速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 655 % | 655 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1002 % | 1002 % | ASTM D882 | ||
| Secant Modulus, MD | 0.278 GPa | 40.3 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.288 GPa | 41.8 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 0.17 | 0.17 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 9.20 g/micron | 234 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 27.7 g/micron | 704 g/mil | ASTM 1922 | ||
| Dart Drop | 4.92 g/micron | 125 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 34.7 MPa | 5030 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 29.1 MPa | 4220 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12.4 % | 12.4 % | ASTM D1003 | ||
| Gloss | 9.0 % | 9.0 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock, Slip, and PPA | ||||
| Minimum Recommended Thickness | 40 µm | ||||