- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 44.0 MPa | 6380 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 46.0 MPa | 6670 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 870 % | 870 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1060 % | 1060 % | ASTM D882 | ||
| Secant Modulus, MD | 0.220 GPa | 31.9 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.224 GPa | 32.5 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 0.70 | 0.70 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.5 g/micron | 267 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 17.5 g/micron | 445 g/mil | ASTM 1922 | ||
| Dart Drop | 32.8 g/micron | 833 g/mil | ASTM D1709 | ||
| Heat Seal Strength Initiation Temperature | 99.0 °C | 210 °F | Sealing Initial Temperature | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 9.0 % | 9.0 % | ASTM D1003 | ||
| Gloss | 13 % | 13 % | ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | PPA | ||||
| Puncture Strength | 30 J/mm | ASTM D5748 | |||