- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 44.0 MPa | 6380 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 46.0 MPa | 6670 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 870 % | 870 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1060 % | 1060 % | ASTM D882 | ||
| Secant Modulus, MD | 0.220 GPa | 31.9 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.224 GPa | 32.5 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.5 g/micron | 267 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 17.5 g/micron | 445 g/mil | ASTM 1922 | ||
| Dart Drop | 32.8 g/micron | 833 g/mil | ASTM D1709 | ||
| Heat Seal Strength Initiation Temperature | 99.0 °C | 210 °F | Sealing Initial Temperature | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 9.0 % | 9.0 % | ASTM D1003 | ||
| Gloss | 13 % | 13 % | ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock, Slip, and PPA | ||||
| Puncture Strength | 30 J/mm | ASTM D5748 | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.