- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 947 % | 947 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1185 % | 1185 % | ASTM D882 | ||
| Secant Modulus, MD | 0.174 GPa | 25.2 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.184 GPa | 26.7 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 0.67 | 0.67 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 11.0 g/micron | 279 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 20.0 g/micron | 508 g/mil | ASTM 1922 | ||
| Dart Drop | 4.55 g/micron | 116 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 47.0 MPa | 6820 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 37.0 MPa | 5370 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 34.8 % | 34.8 % | ASTM D1003 | ||
| Gloss | 4.9 % | 4.9 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock and PPA | ||||
| Minimum Recommended Thickness | 50 µm | ||||