- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM-D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 920 % | 920 % | ASTM-D882 |
| Film Elongation at Break, TD | 1240 % | 1240 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 330 g | 330 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 770 g | 770 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 13.2 g/micron | 335 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 30.8 g/micron | 782 g/mil | ASTM-D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | ASTM-D1709 |
| Dart drop Test | 200 g | 0.441 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 150 MPa | 21800 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 170 MPa | 24700 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM-D1003 |
| Gloss | 121 % | 121 % | Angle 60°; ASTM-D2457 |