- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM-D792 |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1100 % | 1100 % | ASTM-D882 |
| Film Elongation at Break, TD | 1380 % | 1380 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 290 g | 290 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 4.00 g/micron | 102 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 11.6 g/micron | 295 g/mil | ASTM-D1922 |
| Dart Drop | 4.00 g/micron | 102 g/mil | ASTM-D1709 |
| Dart drop Test | 100 g | 0.221 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 140 MPa | 20300 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 150 MPa | 21800 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 35 % | 35 % | ASTM-D1003 |
| Gloss | 52 % | 52 % | Angle 60°; ASTM-D2457 |