- 熔体流动速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM-D792 | ||
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 890 % | 890 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 1110 % | 1110 % | ASTM-D882 | ||
| Elmendorf Tear Strength MD | 270 g | 270 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 590 g | 590 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 7.11 g/micron | 181 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 15.53 g/micron | 394.5 g/mil | ASTM-D1922 | ||
| Dart Drop | 30.26 g/micron | 768.6 g/mil | ASTM-D1709 | ||
| Dart drop Test | 1150 g | 2.54 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 | ||
| 1% Secant Modulus, MD | 270 MPa | 39200 psi | ASTM-D882 | ||
| 1% Secant Modulus, TD | 310 MPa | 45000 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 16 % | 16 % | ASTM-D1003 | ||
| Gloss | 75 % | 75 % | Angle 60°; ASTM-D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Die Opening | 0.180 - 0.250 cm @Temperature 200 - 220 °C | 0.0709 - 0.0984 in @Temperature 392 - 428 °F | Blown Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.5 | 2.0 - 3.5 | Blown Film Extrusion | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 220 | max, Blown Film Extrusion | |||
| Screen Package | 40/60/40 | mesh | |||
| Temperature Profile (°C) | 190-220 | Blown Film Extrusion | |||