- 熔体流动速率 [g/10min]: 29.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 12.0
- 弯曲模量 [MPa]: 370
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM-D729 |
| ESCR 10% Igepal® | 0.80 hour @Thickness 2.00 mm, Temperature 50.0 °C | 0.80 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 29 g/10 min @Load 2.16 kg, Temperature 190 °C | 29 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM-D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM-D638 |
| Elongation at Break | 250 % | 250 % | ASTM-D638 |
| Modulus of Rigidity | 0.320 GPa | 46.4 ksi | ASTM-D747 |
| Flexural Modulus, 1% Secant | 370 MPa | 53700 psi | ASTM-D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.0 °C @Load 1.02 kg | 203 °F @Load 2.25 lb | ASTM-D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM-D746 |