- 熔体流动速率 [g/10min]: 48.0
- 密度 [g/cm3]: 0.931
- 缺口冲击强度: 0.9
- 拉伸强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 543
- 热变形温度 [℃]: 49.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM-D729 |
| ESCR 10% Igepal® | 0.20 hour @Thickness 2.00 mm, Temperature 50.0 °C | 0.20 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 48 g/10 min @Load 2.16 kg, Temperature 190 °C | 48 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | ASTM-D2240 |
| Tensile Strength at Break | 9.00 MPa | 1310 psi | ASTM-D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM-D638 |
| Elongation at Break | 100 % | 100 % | ASTM-D638 |
| Elongation at Yield | 14 % | 14 % | ASTM-D638 |
| Modulus of Rigidity | 0.490 GPa | 71.1 ksi | ASTM-D747 |
| Flexural Modulus, 1% Secant | 543 MPa | 78800 psi | ASTM-D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM-D648 |
| Vicat Softening Point | 97.0 °C @Load 1.02 kg | 207 °F @Load 2.25 lb | ASTM-D1525 |