- 熔体流动速率 [g/10min]: 2.7
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM-D1505 |
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1090 % | 1090 % | ASTM-D882 |
| Film Elongation at Break, TD | 1380 % | 1380 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 60 g | 60 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 320 g | 320 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 1.58 g/micron | 40.1 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 8.42 g/micron | 214 g/mil | ASTM-D1922 |
| Dart Drop | 1.58 g/micron | 40.1 g/mil | ASTM-D1709 |
| Dart drop Test | 60.0 g | 0.132 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 230 MPa | 33400 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 23 % | 23 % | ASTM-D1003 |
| Gloss | 68 % | 68 % | Angle 60°; ASTM-D2457 |