- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.928
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | 2 in per min; ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | 2 in per min; ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | 2 in per min; ASTM D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 g | 300 g | ASTM D1922 |
| Dart drop Test | 100 g | 0.221 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | 2 in per min; ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Gloss | 91 % | 91 % | 45°; ASTM D2457 |