- 熔体流动速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.00 MPa | 1160 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.00 MPa | 1160 psi | 2 in per min; ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | 2 in per min; ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | 2 in per min; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.70 | 0.70 | ASTM D1894 |
| Coefficient of Friction, Static | 1.0 | 1.0 | ASTM D1894 |
| Elmendorf Tear Strength MD | 225 g | 225 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 375 g | 375 g | ASTM D1922 |
| Dart drop Test | >= 1100 g | >= 2.43 lb | 26 in; ASTM D1709 |
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | 2 in per min; ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |