- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 10.3
- 弯曲模量 [MPa]: 0.276
- 热变形温度 [℃]: 40.0
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | <= 1.0 hour @Temperature 50.0 °C | <= 1.0 hour @Temperature 122 °F | F50; Compression molded; ASTM D1693 |
| Melt Index of Compound | 1.85 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.85 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 46 | 46 | Compression molded; ASTM D2240 |
| Tensile Strength at Break | 10.3 MPa | 1500 psi | Compression molded; ASTM D638 |
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | Compression molded; ASTM D638 |
| Elongation at Break | 470 % | 470 % | Compression molded; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Compression molded; ASTM D638 |
| Flexural Modulus | 0.276 GPa | 40.0 ksi | Compression molded; ASTM D790 B |
| Tensile Impact Strength | 147 kJ/m² | 70.0 ft-lb/in² | Compression molded; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 113 °C | 235 °F | Dow Method (DSC) |
| Crystallization Temperature | 100 °C | 212 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | Compression molded; ASTM D648 |
| Vicat Softening Point | 98.9 °C | 210 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | Compression molded; ASTM D746 |