- 密度 [g/cm3]: 0.933
- 拉伸强度 [MPa]: 16.5
- 弯曲模量 [MPa]: 0.572
- 热变形温度 [℃]: 52.2
- 脆化温度 [℃]: -20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Melt Index of Compound | 155 g/10 min @Load 2.16 kg, Temperature 190 °C | 155 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 8.96 MPa | 1300 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 50 % | 50 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.572 GPa | 83.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 105 kJ/m² | 50.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Dow Method (DSC) |
| Crystallization Temperature | 113 °C | 235 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 52.2 °C | 126 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |