- 熔体流动速率 [g/10min]: 32.0
- 密度 [g/cm3]: 0.925
- 弯曲模量 [MPa]: 0.345
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Melt Flow | 32 g/10 min @Load 2.16 kg, Temperature 190 °C | 32 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 - 58 | 52 - 58 | Instantaneous; ASTM D2240 |
| Tensile Strength at Break | 7.93 MPa | 1150 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Modulus | 0.345 GPa | 50.0 ksi | Test Method I, Procedure B (chs speed 0.05 in/min), 1 % Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -76.1 °C | -105 °F | ASTM D746 |