- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 20.0
- 弯曲强度 [MPa]: 15.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 2.5 g/10 min @Load 2.16 kg | 2.5 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.1. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 15.2 MPa | 2200 psi | Molded property |
| Film Tensile Strength at Yield, MD | 17.9 MPa | 2600 psi | |
| Film Tensile Strength at Yield, TD | 17.9 MPa | 2600 psi | |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | Molded property |
| Film Elongation at Break, MD | 480 % | 480 % | |
| Film Elongation at Break, TD | 740 % | 740 % | |
| Elongation at Break | 600 % | 600 % | Molded value |
| Elmendorf Tear Strength MD | 25 g | 25 g | |
| Elmendorf Tear Strength TD | 700 g | 700 g | |
| Elmendorf Tear Strength, MD | 1.00 g/micron | 25.4 g/mil | |
| Elmendorf Tear Strength, TD | 28.0 g/micron | 711 g/mil | |
| Dart Drop | 2.00 g/micron | 50.8 g/mil | |
| Film Tensile Strength at Break, MD | 56.5 MPa | 8190 psi | |
| Film Tensile Strength at Break, TD | 34.5 MPa | 5000 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 119 °C | 246 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 3.2 % | 3.2 % | |
| Gloss | 88 % | 88 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |