- 熔体流动速率 [g/10min]: 80.0
- 密度 [g/cm3]: 0.933
- 缺口冲击强度: 32.0
- 拉伸强度 [MPa]: 11.8
- 弯曲强度 [MPa]: 8.75
- 弯曲模量 [MPa]: 0.553
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | |
| Viscosity | 34000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 34000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 54000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 54000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 77000 cP @Shear Rate 300 1/s, Temperature 190 °C | 77000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 80 g/10 min @Load 2.16 kg | 80 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 8.75 MPa | 1270 psi | |
| Tensile Strength, Yield | 11.8 MPa | 1710 psi | |
| Elongation at Break | 500 % | 500 % | |
| Modulus of Elasticity | 0.327 GPa | 47.4 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.553 GPa | 80.2 ksi | |
| Izod Impact, Notched (ISO) | 32.0 kJ/m² @Temperature -50.0 °C | 15.2 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 101 °C | 214 °F | |