- 熔体流动速率 [g/10min]: 0.72
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.72 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 624 % | 624 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Secant Modulus, MD | 0.203 GPa | 29.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.210 GPa | 30.5 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.12 | >= 0.12 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.0 g/micron | 584 g/mil | ASTM D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % @Thickness 0.0250 mm | 11 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 51 % | 51 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 220 °C | 410 - 428 °F | |