- 熔体流动速率 [g/10min]: 0.57
- 密度 [g/cm3]: 0.92
- 脆化温度 [℃]: -90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.57 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.57 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 830 % | 830 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.50 | >= 0.50 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 7.00 g/micron | 178 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 16.0 g/micron | 406 g/mil | ASTM D1922 |
| Dart Drop | 5.00 g/micron | 127 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Brittleness Temperature | <= -90.0 °C | <= -130 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % @Thickness 0.0250 mm | 8.0 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 55 % | 55 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 220 °C | 410 - 428 °F | |