- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 6.80 g/m²/day | 0.438 g/100 in²/day | 100% Humidity; ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.2 MPa | 1770 psi | ASTM D882 |
| Film Elongation at Break, MD | 680 % | 680 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Film Elongation at Yield, MD | 12 % | 12 % | ASTM D882 |
| Film Elongation at Yield, TD | 4.0 % | 4.0 % | ASTM D882 |
| Elmendorf Tear Strength MD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 470 g | 470 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 28.4 MPa | 4120 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.8 MPa | 4180 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |