- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 5000 ppm | 5000 ppm | |||
| Slip Level | 850 ppm | 850 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.65 MPa | 1400 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.65 MPa | 1400 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 580 % | 580 % | ASTM D882 | ||
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 | ||
| Puncture Energy | 3.13 J | 2.31 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 15.7 g/micron | 400 g/mil | ASTM D1922 | ||
| Dart Drop | 4.09 g/micron | 104 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 53.1 MPa | 7700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 35.3 MPa | 5120 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 193 MPa | 28000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 223 MPa | 32300 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 121 °C | 249 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 15.3 % | 15.3 % | ASTM D1003 | ||
| Gloss | 45 % | 45 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||