- 熔体流动速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.927
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ExxonMobil Method | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.7 MPa | 1700 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 13.1 MPa | 1900 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 | ||
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 | ||
| Puncture Energy | 2.71 J | 2.00 ft-lb | Exxon Mobil Method | ||
| Coefficient of Friction, Dynamic | 0.57 | 0.57 | ExxonMobil Method | ||
| Coefficient of Friction, Static | 0.68 | 0.68 | ExxonMobil Method | ||
| Elmendorf Tear Strength, MD | 6.30 g/micron | 160 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 17.3 g/micron | 440 g/mil | ASTM D1922 | ||
| Dart Drop | 5.51 g/micron | 140 g/mil | ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 53.1 MPa | 7700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 49.0 MPa | 7100 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 202 MPa | 29300 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 333 MPa | 48300 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 122 °C | 252 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 32 % | 32 % | ASTM D1003 | ||
| Gloss | 29 % | 29 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | PPA and Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.