- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.48 MPa | 1230 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 8.62 MPa | 1250 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 660 % | 660 % | ASTM D882 | ||
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 | ||
| Puncture Energy | 1.11 J | 0.817 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 4.72 g/micron | 120 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 13.4 g/micron | 340 g/mil | ASTM D1922 | ||
| Dart Drop | 2.76 g/micron | 70.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 36.5 MPa | 5300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 26.2 MPa | 3800 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 177 MPa | 25700 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 196 MPa | 28400 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 28.7 % | 28.7 % | ASTM D1003 | ||
| Gloss | 22 % | 22 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||