- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.925
- 拉伸强度 [MPa]: 11.72
- 弯曲模量 [MPa]: 0.4275
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | 330 hour | 330 hour | Condition B, 10%; ASTM D1693 | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 11.72 MPa | 1700 psi | ASTM D638 | ||
| Elongation at Break | 350 % | 350 % | ASTM D638 | ||
| Flexural Modulus | 0.4275 GPa | 62.00 ksi | 2% secant; ASTM D790 | ||
| Flexural Modulus, 1% Secant | 483 MPa | 70000 psi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | ASTM D3418 | ||
| Vicat Softening Point | 92.2 °C | 198 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Standard processing antioxidants | ||||
| Form | PELLET | ||||