- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Antiblock Level | 5000 ppm | 5000 ppm | |||
| Slip Level | 1700 ppm | 1700 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.48 MPa | 1230 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 8.62 MPa | 1250 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 660 % | 660 % | ASTM D882 | ||
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 | ||
| Puncture Energy | 1.11 J | 0.817 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 4.72 g/micron | 120 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 13.4 g/micron | 340 g/mil | ASTM D1922 | ||
| Dart Drop | 2.76 g/micron | 70.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 36.5 MPa | 5300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 26.2 MPa | 3800 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 177 MPa | 25700 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 196 MPa | 28400 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 28.7 % | 28.7 % | ASTM D1003 | ||
| Gloss | 22 % | 22 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.