- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.66 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 3500 ppm | 3500 ppm | |||
| Slip Level | 1700 ppm | 1700 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1500 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 520 % | 520 % | ASTM D882 | ||
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 | ||
| Puncture Energy | 1.05 J | 0.775 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 2.76 g/micron | 70.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 17.3 g/micron | 440 g/mil | ASTM D1922 | ||
| Dart Drop | 2.36 g/micron | 60.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 45.8 MPa | 6640 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 27.2 MPa | 3940 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 230 MPa | 33400 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 261 MPa | 37800 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 18.4 % | 18.4 % | ASTM D1003 | ||
| Gloss | 46 % | 46 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||