- 熔体流动速率 [g/10min]: 6.8
- 密度 [g/cm3]: 0.936
- 拉伸强度 [MPa]: 17.2
- 弯曲模量 [MPa]: 0.689
- 热变形温度 [℃]: 59.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D4883 |
| ESCR 100% Igepal® | 300 hour | 300 hour | ASTM D1693 |
| ESCR 10% Igepal® | 60 hour | 60 hour | ASTM D1693 |
| Melt Flow | 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 17.2 MPa | 2500 psi | ASTM D638 |
| Elongation at Yield | 20 % | 20 % | ASTM D638 |
| Flexural Modulus | 0.689 GPa | 100 ksi | 1% secant; ASTM D790 |
| Impact Test | 81.3 J @Thickness 3.17 mm, Temperature -40.0 °C | 60.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM |
| 217 J @Thickness 6.35 mm, Temperature -40.0 °C | 160 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 °C | 138 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 |