- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 5000 ppm | 5000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.7 MPa | 1700 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 13.8 MPa | 2000 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 510 % | 510 % | ASTM D882 | ||
| Film Elongation at Break, TD | 810 % | 810 % | ASTM D882 | ||
| Puncture Energy | 2.94 J | 2.17 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 5.51 g/micron | 140 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 30.7 g/micron | 780 g/mil | ASTM D1922 | ||
| Dart Drop | 45.3 g/micron | 1150 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 61.4 MPa | 8900 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 48.3 MPa | 7000 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 234 MPa | 34000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 283 MPa | 41000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 125 °C | 257 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 15 % | 15 % | ASTM D1003 | ||
| Gloss | 57 % | 57 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||