- 熔体流动速率 [g/10min]: 4.4
- 密度 [g/cm3]: 0.914
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.914 g/cc | 0.0330 lb/in³ | ASTM D1505 |
| Thickness | 24.1 microns | 0.950 mil | |
| Melt Flow | 4.4 g/10 min | 4.4 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 470 % | 470 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Secant Modulus, MD | 0.0760 GPa | 11.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0830 GPa | 12.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 450 g | 450 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 530 g | 530 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.7 g/micron | 474 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.0 g/micron | 558 g/mil | ASTM D1922 |
| Dart Drop | 12.4 g/micron | 316 g/mil | ASTM D1709 |
| Dart drop Test | 300 g | 0.662 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Gloss | 92 % | 92 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |