- 熔体流动速率 [g/10min]: 6.8
- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 18.6
- 弯曲模量 [MPa]: 0.689
- 热变形温度 [℃]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | Condition A, F50; ASTM D1693 |
| ESCR 10% Igepal® | 200 hour | 200 hour | Condition A, F50; ASTM D1693 |
| Melt Flow | 6.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.8 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | 2" (50mm) per min; ASTM D638 |
| Elongation at Yield | >= 11.8 % | >= 11.8 % | 2" (50mm) per min; ASTM D638 |
| Flexural Modulus | 0.689 GPa | 100 ksi | 1.3mm per min; ASTM D790 |
| Impact Test | 61.0 J @Thickness 3.17 mm, Temperature -40.0 °C | 45.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | Low Temperature; ARM |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ASTM D648 |