- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 22.0
- 弯曲强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.710
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | Melt Flow Ratio (I10/I2) is 7.2; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 810 % | 810 % | ASTM D638 |
| Modulus of Elasticity | 0.945 GPa | 137 ksi | ASTM D638 |
| Flexural Modulus | 0.710 GPa | 103 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |