- 熔体流动速率 [g/10min]: 8.3
- 密度 [g/cm3]: 0.963
- 拉伸强度 [MPa]: 27.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| Viscosity | 81 cP @Shear Rate 5000 1/s, Temperature 230 °C | 81 cP @Shear Rate 5000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 |
| 185 cP @Shear Rate 1000 1/s, Temperature 230 °C | 185 cP @Shear Rate 1000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| 304 cP @Shear Rate 300 1/s, Temperature 230 °C | 304 cP @Shear Rate 300 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| Melt Flow | 8.3 g/10 min | 8.3 g/10 min | Melt Flow Ratio (I10/I2) is 7.2; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Modulus of Elasticity | 1.566 GPa | 227.1 ksi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |