- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 690 % | 690 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.172 GPa | 24.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.186 GPa | 27.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 460 g | 460 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 950 g | 950 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.1 g/micron | 460 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 37.4 g/micron | 950 g/mil | ASTM D1922 |
| Dart Drop | 11.4 g/micron | 290 g/mil | ASTM D1709 |
| Dart drop Test | 290 g | 0.639 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | >= 19.0 MPa | >= 2760 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 66 % | 66 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 205 - 245 °C | 401 - 473 °F | |