- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 - 0.928 g/cc | 0.0334 - 0.0335 lb/in³ | B.P. 125 | ||
| Melt Flow | 0.90 - 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 - 1.1 g/10 min @Load 4.76 lb, Temperature 374 °F | B.P. 112 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | >= 12.0 MPa | >= 1740 psi | |||
| Film Tensile Strength at Yield, TD | >= 13.0 MPa | >= 1890 psi | |||
| Film Elongation at Break, MD | >= 650 % | >= 650 % | |||
| Film Elongation at Break, TD | >= 850 % | >= 850 % | |||
| Dart drop Test | >= 80.0 g | >= 0.176 lb | |||
| Film Tensile Strength at Break, MD | >= 42.0 MPa | >= 6090 psi | |||
| Film Tensile Strength at Break, TD | >= 33.0 MPa | >= 4790 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | >= 105 °C | >= 221 °F | At 1 kg | ||
| Descriptive Properties | |||||
| Whiteness Index | >48 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.