- 熔体流动速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.928
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 - 0.932 g/cc | 0.0335 - 0.0337 lb/in³ | ASTM D792 |
| Melt Flow | 3.8 - 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.8 - 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ISO 1184 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ISO 1184 |
| Film Elongation at Break, MD | >= 785 % | >= 785 % | ISO 1184 |
| Film Tensile Strength at Break, MD | >= 33.0 MPa | >= 4790 psi | ISO 1184 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 1184 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | >= 104 °C | >= 219 °F | ASTM D1525 |