- 熔体流动速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.928
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 - 0.932 g/cc | 0.0335 - 0.0337 lb/in³ | ASTM D1505 |
| Melt Flow | 3.8 - 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.8 - 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 785 % | 785 % | ASTM D882 |
| Film Elongation at Break, TD | 926 % | 926 % | ASTM D882 |
| Film Tensile Strength at Break, MD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 A-61 |
| Gloss | 87 % | 87 % | PU Meter, 45°C Head; ASTM D2456-70 |