- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D 792 | ||
| Thickness | 25.0 microns | 0.984 mil | As tested for properties on this data sheet | ||
| 12.7 - 76.0 microns | 0.500 - 2.99 mil | Recommended range for processing | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 540 % | 540 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 450 g | 450 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 12.0 g/micron | 305 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 18.0 g/micron | 457 g/mil | ASTM D 1922 | ||
| Dart Drop | 16.0 g/micron | 406 g/mil | ASTM D 1709/A | ||
| Dart drop Test | 400 g | 0.882 lb | F50; ASTM D 1709/A | ||
| Film Tensile Strength at Break, MD | 46.0 MPa | 6670 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 42.0 MPa | 6090 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 126 MPa | 18300 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 132 MPa | 19100 psi | ASTM D 882 | ||
| Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | Temperature at which a 2-mil film achieves a seal strength of 4.4N/13mm. Tested at 0.5s dwell, 0.27 N/mm² bar pressure, 305mm/min. pull speed. | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | LDPE blended; ASTM D 1003 | ||
| 16 % | 16 % | 100% LLDPE; ASTM D 1003 | |||
| Gloss | 37 % | 37 % | At 45°, 100% LLDPE; ASTM D 2457 | ||
| 72 % | 72 % | At 45°, LDPE blended; ASTM D 2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 180 - 200 °C | 356 - 392 °F | Recommended | ||
| Die Opening | 0.0889 - 0.216 cm | 0.0350 - 0.0850 in | Recommended range | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Optimum range | ||
| Descriptive Properties | |||||
| Low Friction Puncture | 79 (J/mm) | NOVA Chemicals test method | |||