- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D 792 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.20 MPa | 1330 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 9.50 MPa | 1380 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 303 g | 303 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 588 g | 588 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 12.1 g/micron | 307 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 23.5 g/micron | 597 g/mil | |||
| Dart drop Test | 560 g | 1.23 lb | 22; ASTM D 1709/A | ||
| Film Tensile Strength at Break, MD | 61.0 MPa | 8850 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 140 MPa | 20300 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 170 MPa | 24700 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | ASTM D 1003 | ||
| Gloss | 65 % | 65 % | at 45°; ASTM D 2457 | ||
| Descriptive Properties | |||||
| Low Friction Puncture (J/mm) | 89 | NOVA Chemicals Test Method | |||