- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.916 - 0.920 g/cc | 0.0331 - 0.0332 lb/in³ | Base Resin; ASTM D1505 | ||
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1283/L | ||
| 24 - 36 g/10 min @Load 21.6 kg, Temperature 190 °C | 24 - 36 g/10 min @Load 47.6 lb, Temperature 374 °F | Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | >= 50.0 MPa | >= 7250 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | >= 35.0 MPa | >= 5080 psi | ASTM D882 | ||
| Film Elongation at Break, MD | >= 700 % | >= 700 % | ASTM D882 | ||
| Film Elongation at Break, TD | >= 950 % | >= 950 % | ASTM D882 | ||
| Tensile Modulus | >= 0.130 GPa | >= 18.9 ksi | 2% sec, MD; ASTM D882 | ||
| >= 0.140 GPa | >= 20.3 ksi | 2% sec, TD; ASTM D882 | |||
| Elmendorf Tear Strength, MD | >= 9.45 g/micron | >= 240 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | >= 18.9 g/micron | >= 480 g/mil | ASTM D1922 | ||
| Dart drop Test | >= 210 g | >= 0.463 lb | ASTM D1709 | ||
| Descriptive Properties | |||||
| Gel Content (pcs./m²) | 0 | > 1mm | |||
| 245 | (0.2-0.5)mm | ||||
| 250 | > 0.2mm (totally) | ||||
| 5 | (0.5-1.0)mm | ||||